Hastelloy C2000 - bu Ni-Cr-Mo qotishmasining yangi turi. C4 qotishmasi asosida xromning tarkibi yaxshilanadi va mis qo'shilishi oksidlanishga chidamliligi va qotishma qaytaruvchi vositasining korroziyaga qarshi qobiliyatini yaxshilaydi. Hozirda Hastelloy C2000 H2SO4 ning korroziyaga chidamliligi yaxshi bo'lgan qotishmalar seriyasidir, ammo kristallararo korroziyaga chidamliligi C4 qotishmasiga o'xshamaydi
Qotishma | C | Kr | Ni | Fe | Mo | W | Cu | Si | Mn | P | S |
Hastelloy C-2000 | -0.01 | 22.0-23.0 | muvozanat | -3.0 | 15.0-17.0 | 3.0-4.5 | 1.3-1.9 | .00.08 | -0.5 | -0.02 | .00.08 |
Zichlik
|
8,5 g / sm³
|
Erish nuqtasi
|
1260-1320 ℃
|
Qalinligi (mm) |
Uzatilish kuchi (Mpa) | Hosildorlik kuchi σ0,2 (Mpa) |
Uzayish (50,8 mm) (%) |
1.6 | 752 | 358 | 64.0 |
3.18 | 765 | 393 | 63.0 |
6.35 | 779 | 379 | 62.0 |
12.7 | 758 | 345 | 68.0 |
25.4 | 752 | 372 | 63.0 |
ASTM B564, ASTM B574, ASTM B575, ASTM B619, ASTM B622, ASTM B366
Bar / novda | Sim | Ip / lasan | Plitalar / plitalar | Quvur / quvur |
Korroziyaga chidamliligi, shu jumladan oltingugurt kislotasi xloridli gidroflorik kislota fosfat organik xlor gidroksidi metall yorig'i korroziya chuqurchasi, stress korroziyasining yorilishi.
C-2000 qotishmasi sanoat standartiga qaraganda C-276 qotishmasiga qaraganda chuqurlik va yoriqlar korroziyasiga nisbatan yaxshiroq qarshilik ko'rsatadi.
Hastelloy C-2000 ning C276 ga o'xshashligini payvandlash va ishlov berish shakllanishi qotishma konstruktsiyasidagi ikkilamchi muammoni hal qiladi.
Metallurgiya barqarorligini yo'qotmasdan, xrom va molibden va mis tarkibidagi birikmalar bilan birgalikda atrof-muhitni pasaytirishga qarshi mukammal korroziyaga chidamliligi.
• Kimyoviy jarayonlar sanoatining reaktori, issiqlik almashinuvchisi, ustunlar va quvur.
• farmatsevtika sanoatining reaktori va quritgichi.
• Baca gazini desulfurizatsiya qilish tizimi.