C |
S |
P |
Si |
Mn |
Ti |
Co |
Kr |
Fe |
Zr |
Cu |
B |
Al |
≤ |
||||||||||||
0.13 |
0,015 |
0,02 |
0.8 |
0.4 |
2.0-3.0 |
15.0-21.0 |
18.0-21.0 |
-1.5 |
.10.15 |
.20.2 |
-0.02 |
1.0-2.0 |
Zichlik (g / sm)3) |
Erish nuqtasi (℃) |
Issiqlik o'tkazuvchanligi (Vt / m · ℃) |
Elastik modul (MPa) |
Issiqlik kengayish koeffitsienti (10-6℃-1) |
8.2 | 1400 | 21,76 (100 ℃) | 225 | 12,71 (20-100 ℃) |
Issiqlik bilan ishlov berish | Mustahkamlik chegarasi (MPa) |
Hosildorlik kuchi (MPa) |
Uzayish (%) |
Eritmani davolash | 820 | 590 | 8 |
Bar / novda | Sim | Ip / lasan | Plitalar / plitalar | Quvur / quvur |
BS HR2, HR501, HR502 va HR503; SAE AMS 5829; AECMA PrEN 2295, 2296
2297, 2400, 2401, 2669 va 2670.
|
BS HR202, AECMA PrEN 2298
|
BS HR402, AECMA PrEn 2299
|
Ushbu qotishma asosan mainly'i3 (Ti 、) fazasini kuchaytiradi. Kobalt nikel asosli superalloyning qarish deformatsiyasi, tarkibida yuqori miqdordagi kobalt va
turli xil mustahkamlovchi element, 815 ~ 870 in da yuqori tortishish kuchi va sudralish qarshiligi, oksidlanish va korroziyaga chidamliligi,
sovuq va issiqda o'zgaruvchan, yuqori charchoq kuchi va yaxshi shakllanuvchanligi va payvandlanuvchanligini ko'rsatib turadi
• Turbinali dvigatel turbinali disk • Pichoq • Shlangi halqa va elastik element
• yuqori haroratli mahkamlagichlar • Qopqoq halqasi va elastik elementi va boshqalar